Cataphoretic electrodeposition baths containing water-soluble lead salts

ABSTRACT

Cataphoretic electrodeposition baths for coating ferrous metal articles, particularly untreated ferrous metal articles, are disclosed. The baths comprise aqueous dispersions of cationic electrodepositable resins and lead ions which are introduced into said bath by the addition of water-soluble lead compounds. Coatings electrodeposited on ferrous metal articles from such baths have excellent corrosion resistance.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to cataphoretic electrodeposition baths and to the use of these baths in cationic electrodeposition of ferrous metal articles, particularly untreated ferrous metal articles.

2. Brief Description of the Prior Art

Electrodeposition of aqueous organic coatings has risen to industrial prominence in recent years. The process has many advantages including uniformity and completeness of coating, even on intricate shapes. The process results in labor savings and pollution abatement. Virtually any electrically conductive substrate can be coated. However, the process has been primarily employed to prime ferrous metal substrates.

Particular interest has recently arisen in cationic electrodeposition coatings, that is, coatings which deposit on the cathode, since when the article is the cathode, there is greatly reduced metal ion dissolution which commonly causes poor corrosion resistance and staining in certain anionic systems.

Examples of suitable cationic electrodepositable resins are those described in U.S. Pat. Nos. 3,799,854 and 3,984,299, both to Jerabek, and 3,947,338 and U.S. Patent Application Ser. No. 648,982, filed Jan. 14, 1976, both to Jerabek, Marchetti and Zwack. The cationic solubilizing groups in these resins are amine acid salts. Also suitable for cationic electrodeposition are quaternary ammonium salt group-containing resins such as those described in U.S. Pat. Nos. 3,962,165 and 4,001,156 to Bosso and Wismer.

Although cationic electrodepositable resins offer significant improvement over anionic electrodepositable resins, it has been noticed that for maximum corrosion resistant coatings over ferrous metal, the metal must be pretreated before it is electrocoated. Examples of pretreatments are the phosphating treatments which include iron phosphating, mixed iron and calcium phosphating and zinc phosphating. Such pretreatments may optionally be followed by a chromic acid rinse. The pretreatment operations, although employed on many industrial electrodeposition lines, are undesirable for a number of reasons. First of all, pretreatments are expensive. Besides the cost of the chemicals themselves, a considerable capital investment is required for equipment. In addition, pretreatments cause pollution problems, the solutions of which add to their expense.

Another and perhaps more important problem associated with pretreatment is the difficulty in applying a uniform pretreatment. With complexed shaped articles, such as automobile rocker panels and the inside surfaces of doors, it is very difficult to apply uniformly the pretreatment chemical. Also, the pretreatment equipment itself may not be operating in a uniform manner resulting in some areas being poorly pretreated. These areas will be the first to corrode and will ruin the entire article. Also, in the case of pretreating steel, there are many grades of steel which may require different degrees of pretreatment. Also, the quality and condition of the steel is important and may not be accurately known by the one doing the pretreatment. Steel of poor quality such as oily steel or steel contaminated with some impurity may detrimentally affect or at least reduce the effect of the pretreatment.

Therefore, it would be desirable to provide a cationic electrodeposition bath which can do away with the need for chemical pretreatment or at least compensate for any shortcomings or deficiencies in the pretreatment process.

SUMMARY OF THE INVENTION

In accordance with the present invention, an electrodeposition bath which contains an aqueous dispersion of a cationic electrodepositable resin is provided. The bath includes lead ions (Pb⁺²) which are introduced into the bath by the addition of a water-soluble lead compound. The addition of such a lead compound, in a sufficient amount, has been found to increase the corrosion resistance of a coating cathodically electrodeposited on a ferrous metal surface, particularly an untreated or poorly treated ferrous metal surface, over a comparable coating electrodeposited from a similar bath which does not contain the lead ions. In addition, it has also been found that the lead ions retard corrosion of the iron parts of the electrodeposition bath.

The invention also provides for a method of cationic electrodeposition employing the electrodeposition bath described above to which has been added the water-soluble lead salts.

PERTINENT PRIOR ART

Belgian Pat. No. 836,333 discloses electrodeposition baths containing cationic electrodepositable resins. The baths are modified by adding water-soluble salts whose potential in the cationic electrochemical series is higher than the potential of the ferrous metal surface being electrocoated in the bath. Among the metal salts specifically disclosed are salts of copper, cobalt, cadmium, zinc, nickel, tin and antimony. Lead is specifically not mentioned in the patent as being useful. Surprisingly, it has been found in the practice of the present invention that water-soluble lead compounds are superior to many of the water-soluble salts disclosed in the Belgian patent in terms of providing for improved corrosion-resistant coatings.

U.S. Pat. No. 3,799,854 to Jerabek discloses cationic electrodeposition baths which contain amine salt group-containing resinous binders. Besides the binders, the paint in these baths contain various pigments including basic lead silicate. The lead silicate is introduced into the bath in the form of a pigment paste.

The electrodeposition baths of the present invention differ from those of Jerabek in that they contain lead introduced into the bath from the addition of a water-soluble lead compound, whereas the lead in Jerabek is in the form of a water-soluble lead pigment. Although some of the insoluble lead may dissolve in the bath over a period of time if the pH is low enough, the amount would probably not be sufficient to provide for optimum corrosion resistance. Also, the amount would depend on the pH of the bath. In fresh baths based on quaternary ammonium salt group-containing resins which have a pH of about 7, insufficient amounts of lead pigment are dissolved.

DETAILED DESCRIPTION

As mentioned above, the lead compound which is added to the electrodeposition bath is water soluble which means the lead compound is soluble in water having a pH of 7 to the extent of at least one percent by weight based on total solution weight. Suitable lead compounds are lead salts of organic acids such as acetic and lactic acids. The lead salts of strong mineral acid such as hydrochloric acid and nitric acid are not preferred because of poor coating properties. Examples of other suitable lead compounds include lead salts or complexes of amino acids such as glycine, sarcosine; ethylene diamine tetra-acetic acid, N-(2-hydroxyethyl) ethylene dinitrilo triacetic acid, citric acid and ascorbic acid.

Many of the desirable lead compounds are commercially available products. However, many of the salts can be prepared by reacting lead oxide with the appropriate acid in aqueous medium.

The amount of lead compound which is added to the electrodeposition bath should be that sufficient to provide for improved corrosion resistance on a ferrous metal particularly an untreated or poorly treated ferrous metal article which is cathodically electrodeposited in said bath. The improved degree of corrosion resistance is determined by comparing salt spray exposures of coatings deposited from electrodeposition baths in accordance with the present invention with coatings deposited from electrodeposition baths to which no water-soluble lead salt has been added. Although very low amounts of lead will provide some protection, the amount of water-soluble lead compound which is added to the bath is usually at least 50 and preferably from 100 to 3000 and more preferably from 200 to 3000 parts per million (by weight) of lead in the bath based on total bath weight. Lead levels above 3000 parts per million do not offer any significant advantage in terms of corrosion protection and as the level of soluble lead in the bath increases, properties such as film builds, rupture voltage and bath conductivities suffer.

The addition of the water-soluble lead compound to the electrodeposition bath can be by adding the soluble lead compound directly to the electrodeposition bath containing pigment and resin or to a high solids paint which must be thinned with water to form the bath or by adding the soluble lead compound to the aqueous resinous dispersion or pigment dispersion before the bath is formulated. As the electrodeposition proceeds, the lead compound should be replenished since it is consumed during the course of the electrodeposition.

The metallic articles which are coated in the process of the invention are ferrous metals such as iron, steel, and various alloys thereof with other metals. The invention has particular utility with untreated ferrous metals such as cold rolled steel. By untreated is meant the ferrous metal has not been pretreated with chemicals which enhance the corrosion resistance of the metal. Examples of such pretreatments are the phosphating and chromating treatments mentioned above. However, the invention is also applicable to such pretreated ferrous metals, particularly poorly treated ferrous metals.

The cationic electrodepositable resins which can be used in the practice of the invention include amine salt group-containing resins which are well known in the art for cationic electrodeposition. An example of suitable resinous systems are those disclosed in U.S. Pat. No. 3,799,854 to Jerabek. Particularly preferred amine salt group-containing resins are the reaction products of an organic polyepoxide and a secondary amine. The resinous reaction product is solubilized with acid to provide the amine salt groups. Such resins are described in U.S. Pat. No. 3,984,299 to Jerabek. Usually these amine salt group-containing resins are used in combination with a blocked isocyanate curing agent. In one embodiment, the isocyanate is fully blocked. The above immediately-mentioned two patents describe such systems. Also, the isocyanate can be partially blocked and reacted with the resin to form a one-component system. Such a resinous system is described in U.S. Pat. No. 3,947,358 to Jerabek and Marchetti.

A particularly preferred amine salt group-containing resin is one which contains latent primary amine groups blocked by ketimine functionality. Such a resin is described in U.S. Pat. No. 3,947,339 to Jerabek, Marchetti and Zwack.

Besides amine salt group-containing resins, quaternary ammonium salt group-containing resins can also be employed. Examples of these resins are those formed from reacting an organic polyepoxide such as a polyglycidyl ether of a polyphenol with a tertiary amine acid salt. Such resins are described in U.S. Pat. Nos. 3,962,165, 3,975,346 and 4,001,156 to Bosso and Wismer. In one preferred embodiment, the quaternary ammonium salt group-containing resin contains blocked isocyanate moieties. Resinous systems of this type are described in U.S. Pat. No. 3,935,087 to Jerabek and Marchetti.

Examples of other cationic resins are ternary sulfonium salt group-containing resins such as those described in U.S. Pat. No. 3,793,278 to DeBona.

For electrodeposition, the above-described resinous reaction products are dispersed in water to about a 1 to 30 percent by weight resin solids aqueous dispersion. The term "aqueous dispersion" as used within the context of the present invention is intended to cover 2-phase, translucent, aqueous-resinous systems, especially those in which the aqueous phase forms the continuous phase, and is also intended to cover homogeneous aqueous solutions which appear optically clear. The aqueous dispersions of the present invention have dispersed phases which have average particle size diameters of about 0.1 to 5 microns. The dispersed phase may be spherical or elongated in shape or actually invisible by microscopic investigation.

The products can be employed as such to electrodeposited clear films, but ordinarily they are used as vehicles along with the pigment composition. The pigment composition used may be any of the conventional types, for example, iron oxides, lead silicate, strontium chromate, carbon black, titanium dioxide, talc, barium sulfate and the like, as well as combinations of these and similar pigments. Color pigments such as cadmium yellow, cadmium red, phthalocyanine blue, chromic yellow, toluidine red, hydrated iron oxides and the like may also be included. Dispersing agents which should be of the non-ionic or cationic type of a combination of these types may optionally be employed. A particularly preferred dispersing agent is the resinous pigment grinding vehicle disclosed in U.S. Pat. No. 4,007,154 to Schimmel et al.

Usually the pigment and dispersing agent are bound together to make a paste and this is blended with a major portion of the vehicle to produce a coating composition.

There may also be included in the coating composition additives such as anti-oxidants, wetting agents, dryers, anti-foaming agents, suspending agents and the like. It is often desirable to include small amounts of water-miscible organic solvents, which may be added to the resinous vehicle to aid in handling and processing. Examples of such solvents are 4-methoxy-4-methyl-pentanone-2, and other solvents such as dioxane and glycol ethers can be used.

It has been found in most instances that desirable coatings are obtained using pigmented compositions containing weight ratios of pigment to vehicle of 1.5:1 or less and preferably less than about 1:1. If the composition has too high a pigment-to-vehicle ratio, the electrodeposition film may deposit with poor flow characteristics.

In formulating the water-dispersed compositions, ordinary tap water may be employed. However, such water may contain a relatively high level of cations, which, while not ordinarily rendering the process inoperative, may result in variations in the properties of the baths when used for electrodeposition. In such cases, it is often desirable to utilize deionized water from which the free ions have been removed, as by passage through an ion exchange resin.

In the electrodeposition process employing the aqueous coating compositions described above, the aqueous composition is placed in contact with an electrically conductive anode and an electrically conductive cathode, with the surface to be coated being the cathode. Upon passage of the electric current between the anode and the cathode, while in contact with the bath containing the coating composition, an adherent film of the coating composition is deposited on the cathode. This is in contrast to the processes utilizing polycarboxylic acid resins which deposit on the anode, and many of the advantages described in the process of the present invention are in a large part attributed to this cathodic deposition.

The conditions under which electrodeposition is carried out are, in general, similar to those used in electrodeposition of other types of coatings. The applied voltage may be varied greatly and can be, for example, as low as one volt or as high as several thousand volts, although typically between 50 volts and 500 volts are employed. Current density is usually between about 1.0 ampere and 15 amperes per square foot and tends to decrease during electrodeposition.

After deposition, the coating is cured at elevated temperatures by any convenient method, such as baking in ovens or with banks of infrared heat lamps. Curing temperatures depend principally on the curing agent employed, and when the curing agent is a blocked isocyanate such as described above, curing is usually accomplished at between 75° to 300° C.

The invention will be described further in conjunction with several examples showing the method and practice of the invention. These examples, however, are not to be construed as limiting the invention to their details.

EXAMPLES 1-7

A series of experiments were conducted involving the addition of various water-soluble lead, nickel, zinc and copper salts to aqueous dispersions of cationic electrodepositable resins. The resins were then electrodeposited onto untreated steel panels; the coatings were baked and evaluated for corrosion resistance.

The cationic electrodepositable resin was an amine salt group-containing resin and was prepared from the following charge:

    ______________________________________                                         Ingredient              Parts by Weight                                        ______________________________________                                         EPON 1001.sup.1         122                                                    methyl butyl ketone     42.5                                                   monourethane of 2,4-toluene diisocyanate.sup.2                                 (95% solids in methyl butyl ketone)                                                                    83.0                                                   dibutyltin dilaurate    0.18                                                   diketimine of diethylene triamine.sup.3                                                                9.9                                                    diethylamine            8.0                                                    JEFFAMINE D-1000.sup.4  21.9                                                   hexyl CELLOSOLVE.sup.5  24.1                                                   deionized water         356                                                    lactic acid (88% in water)                                                                             13.1                                                   ______________________________________                                          .sup.1 EPON 1001 - polyglycidyl ether of Bisphenol A possessing an             equivalent weight of 492 per epoxy group, commercially available from          Shell Chemical Company.                                                        .sup.2 2-ethylhexylmonourethane of 2,4-toluene diisocyanate prepared by        adding 1953 parts of 2-ethylhexanol to an agitated mixture of 2610 parts       of 2,4-toluene diisocyanate and 2 parts of methyl butyl ketone over            approximately a 3-hour period with external cooling to maintain the            reaction temperature below 18° C. After the addition was complete,      the product was stored under dry nitrogen until used.                          .sup.3 Diketimine derived from one mole of diethylene triamine and two         moles of methyl isobutyl ketone, commercially available from Shell             Chemical Company as curing agent H-1.                                          .sup.4 Polyoxypropylene diamine having a molecular weight of about 1000,       commercially available from Jefferson Chemical Company.                        .sup.5 Monohexyl ether of ethylene glycol.                               

The cationic electrodepositable resin was prepared as follows: In a suitable reaction vessel, the EPON 1001 was dissolved in the methyl butyl ketone and refluxed for about one hour to remove any water present by the use of a decanting trap in the distillate return line. After cooling to 100° C., the 2-ethylhexyl monourethane of 2,4-toluene diisocyanate and the dibutyltin dilaurate catalyst were added and the reaction mixture heated to 115° C. for about one-half hour until all the NCO was consumed as indicated by an IR scan.

The batch was then cooled to 80° C. and the Shell H-1 added followed by the addition of the diethylamine. The resulting exotherm was controlled by external cooling, keeping the temperature below 95° C. After holding for 35 minutes, the JEFFAMINE D-1000 was then added and the batch heated to 110° C. and held for about three hours at which time the hexyl CELLOSOLVE was added. The reaction mixture was then thinned with deionized water and acidified with the lactic acid to form the cationic resin which had a solids content of about 37 percent.

The cationic electrodepositable resin prepared as described above was diluted with additional deionized water to form an approximately 12 percent solids electrodeposition bath. To six separate portions of the bath were added sufficient lead lactate, nickel lactate, lead acetate, zinc acetate, nickel and copper acetate to give baths containing 0.5 percent by weight (based on resin solids) of the respective metals. One bath with no added metal salt served as a control.

Untreated steel panels were then cathodically electrodeposited in these baths at standard electrocoating conditions as reported in Table I below. The coatings were baked for 20 minutes at 400° F. (204° C.); the baked coatings were scribed with an "X" and placed in a salt spray chamber at 100° F. (38° C.) at 100 percent relative humidity atmosphere of a 5 percent by weight aqueous sodium chloride solution for the period of time shown in Table I below, after which time the creepage from the scribe mark was measured and is also reported in Table I below.

                                      Table I                                      __________________________________________________________________________     Metal Salt Addition to Cationic Electrodeposition Baths                                                         Salt Spray                                    Example      Coating                                                                             Coating Time                                                                          Film Thickness                                                                         Exposure Time                                                                          Scribe Creepage                       No.  Metal Salt                                                                             Voltage                                                                             in seconds                                                                            in mils in days in inches                             __________________________________________________________________________     1    none, control                                                                          100  90     0.8     13      > 1/8                                 2    lead lactate                                                                           100  90     1.0     13      < 1/16                                3    nickel lactate                                                                         100  90     0.8     13       1/4                                  4    lead acetate                                                                           200  90     0.16    10       0                                    5    zinc acetate                                                                           200  90     0.40    10      > 1/8                                 6    nickel acetate                                                                         200  90     0.35    10      1/16-1/8                              7    Copper acetate                                                                         200  90     0.20    10      < 1/16                                __________________________________________________________________________

EXAMPLES 8-16

A series of experiments were conducted to show the effect of the addition of various amounts of water-soluble lead salts to cationic electrodeposition baths. It was found that as little as 500 parts per million water-soluble lead based on resin solids gave good corrosion resistance on untreated steel. Above this level, corrosion resistance was not significantly improved, and film builds, throwpower and electrodeposition bath conductivity suffered as the amount of lead increased.

In addition, two experiments were conducted with water-soluble copper and manganese salts and these were found to give unacceptable coating properties.

The resin was prepared as generally described above in connection with Examples 1-7 and had a solids content of about 37 percent.

A cationic pigment dispersant was prepared by heating 744.2 parts of stearyl glycidyl ether (Procter and Gamble's EPOXIDE 45) and 166.6 parts of ethylene glycol monobutyl ether to about 50° C. and adding 150.2 parts of n-methylethanolamine over a 30-minute period with external cooling to keep the batch temperature below 100° C. When all the amine was added, the batch was held an additional hour at 100° C. before cooling and storage.

To prepare a grinding vehicle from this cationic pigment dispersant, 188 parts were blended with 40 parts of 88 percent aqueous lactic acid, 440 parts of deionized water and 132 parts of ethylene glycol monobutyl ether.

To prepare a pigment paste, 90 parts of this grinding vehicle were blended with 4 parts of an acetylenic alcohol defoamer (SURFYNOL 104-A), 60 parts of phthalocyanine blue, 140 parts of iron oxide brown and 306 parts of deionized water, and the resultant slurry ground in a Jiffy mill to a Hegman No. 7.

The cationic electrodepositable resin of Examples 1-7 and the pigment paste prepared as described above were combined with deionized water and additional dibutyltin dilaurate catalyst in the following charge ratio to form a cationic electrodepositable paint:

    ______________________________________                                         Ingredient           Parts by Weight                                           ______________________________________                                         cationic resin       1053                                                      deionized water      840                                                       dibutyltin dilaurate 7.4                                                       pigment paste        228                                                       deionized water      1672                                                      ______________________________________                                    

The resin and dibutyltin dilaurate were mixed in a Cowles mixer for one hour and diluted with the first portion of deionized water. The pigment paste was then added followed by final dilution with the second portion of deionized water. The paint had a solids content of about 12 percent.

Nine electrodeposition baths, including a control, were prepared from the above-described paint. To six of the electrodeposition baths were added increasing amounts of lead acetate. Copper acetate was added to one bath and manganese acetate was added to the final bath. The amount of soluble salts added to the bath is reported in Table II below. Untreated steel panels were electrodeposited in these baths at 250 volts for two minutes. The film builds and appearance of the coatings are reported in Table II below. Also reported is the Ford throwpower, rupture voltage and conductivity of the various electrodeposition baths.

                                      Table II                                     __________________________________________________________________________     Cationic Electrodeposition Bath Containing Various Types and Amounts of        Water-Soluble Salts                                                                                    Ford                                                   Example                                                                             Parts per Million Metal                                                                     Film Builds                                                                          Throwpower                                                                            Rupture                                         No.  Derived from Soluble Salt                                                                   in mils                                                                              inches Voltage                                                                             Conductivity                                                                          Coating Quality                     __________________________________________________________________________      8       0        0.50  81/4   360  1040   smooth                               9    500 - lead  0.40  81/4   300  1200   smooth                              10   1000 - lead  0.40  8      300  1280   smooth                              11   1500 - lead  0.30  73/4   300  1310   smooth                              12   2000 - lead  0.27  --     300  1380   smooth                              13   2500 - lead  0.24  --     300  1380   smooth                              14   3000 - lead  0.20  --     280  1450   smooth                              15   1250 - copper                                                                               0.30  --     300  1350   rough                               16   1250 - manganese                                                                            0.30  --     250  2420   rough                               __________________________________________________________________________

EXAMPLES 17-32

A first series of experiments was conducted to show the effect of adding a water-soluble lead salt to a cationic paint based on a quaternary ammonium salt group-containing resin.

The quaternary ammonium salt group-containing resin was prepared from the following charge:

    ______________________________________                                         Ingredient              Parts by Weight                                        ______________________________________                                         EPON 829                5428.3                                                 Bisphenol A             1752.3                                                 2-ethylhexanol monourethane of 2,4-                                            toluene diisocyanate, 95% in methyl -isobutyl ketone                                                   3900.8                                                 PCP-0200.sup.1          1424.8                                                 TEXANOL.sup.2           1167.3                                                 dimethyl ethanolamine   25.8                                                   lactic acid (88% in water)                                                                             52.3                                                   ethylene glycol phenyl ether                                                                           1830.5                                                 ethylene glycol ethyl ether                                                                            857.0                                                  FOAMKILL 639.sup.3      66.5                                                   dimethyl cyclohexyl amine lactate (75% in                                      water)                  1600.7                                                 deionized water         857.0                                                  ______________________________________                                          .sup.1 Polycaprolactone diol commercially available from Union Carbide         Corporation having a molecular weight of 530.                                  .sup.2 2,2,4-trimethyl-penlanediol monoisobutyrate.                            .sup.3 A hydrocarbon oil-containing inert diatomaceous earth.            

The EPON 829 and Bisphenol A were charged to a reaction vessel and heated to 150° C. and allowed to exotherm to 202° C. The reaction mixture was cooled to 125° C. and the 2-ethylhexyl monourethane added. The reaction mixture was cooled to 120° C. and held for one hour followed by the addition of TEXANOL, PCP-0200 and the dimethyl ethanolamine. The reaction mixture was heated to 125° C. and held for 81/2 hours followed by the addition of the glycol ethers, FOAMKILL 639, lactic acid, dimethyl cyclohexyl amine lactate, and deionized water. The reaction mixture was cooled to 85° C. and held for two hours followed by cooling to room temperature.

A pigment grinding vehicle was prepared from the following charge:

    ______________________________________                                         Ingredient           Parts by Weight                                                                            Solids                                        ______________________________________                                         EPON 829.sup.1       710.0       681.2                                         Bisphenol A          289.6       289.6                                         2-ethylhexanol monourethane of 2,4-                                            toluene diisocyanate in methyl                                                 isobutyl ketone      406.4       386.1                                         quaternizing agent.sup.2                                                                            496.3       421.9                                         deionized water       71.2       --                                            butyl CELLOSOLVE.sup.3                                                                               56.8       --                                            ______________________________________                                          .sup.1 Epoxy resin solution made from reacting epichlorohydrin and             Bisphenol A having an epoxy equivalent of approximately 193-203,               commercially available from Shell Chemical Company.                            .sup.2 Quaternizing agent was prepared from the following charge:        

    Ingredient           Parts by Weight                                                                            Solids                                        ______________________________________                                         2-ethylhexanol half-capped                                                     toluene diisocyanate in                                                        methyl isobutyl ketone                                                                              320.0       304                                           dimethyl ethanolamine                                                                                87.2       87.2                                          aqueous lactic acid solution                                                                        117.6       88.2                                          butyl CELLOSOLVE      39.2       --                                            ______________________________________                                          2-ethylhexanol half-capped toluene diisocyanate was added to the dimethyl      ethanolamine in a suitable reaction vessel at room temperature. The            mixture exothermed and was stirred for one hour at 80° C. Lactic        acid was then charged, followed by the addition of butyl cellosolve. The       reaction mixture was stirred for about one hour at 65° C. to form       the desired quaternizing agent.                                                .sup.3 Ethylene glycol monobutyl ether.                                  

The EPON 829 and Bisphenol A were charged under a nitrogen atmosphere to a suitable reaction vessel and heated to 150°-160° C. to initiate an exotherm. The reaction mixture was permitted to exotherm for 1 hour at 150°-160° C. The reaction mixture was then cooled to 120° C. and the 2-ethylhexanol half-capped toluene diisocyanate added. The temperature of the reaction mixture was held at 110°-120° C. for one hour, followed by the addition of the butyl CELLOSOLVE. The reaction mixture was then cooled to 85°-90° C., homogenized and then charged with water, followed by the addition of the quaternizing agent. The temperature of the reaction mixture was held at 80°-85° C. until an acid value of one was obtained.

A pigment paste, employing the pigment grinding vehicle described immediately above, was prepared from the following charge:

    ______________________________________                                         Ingredient           Parts by Weight                                           ______________________________________                                         resinous grinding vehicle                                                                           12.2                                                      coal dust            15.8                                                      basic lead silicate  1.9                                                       strontium chromate   1.0                                                       dibutyltin oxide     0.68                                                      deionized water      23.6                                                      ______________________________________                                    

The paste was ground in a sand mill to a Hegman No. 7 grind.

A cationic electrodepositable paint was prepared from the following charge:

    ______________________________________                                         Ingredient               Parts by Weight                                       ______________________________________                                         quaternary ammonium salt group-                                                containing resin         1580                                                  PARAPLEX WP-1, plasticizer (Rohm and Haas)                                                              36                                                    deionized water          3800                                                  pigment paste            682                                                   deionized water          1102                                                  ______________________________________                                    

The quaternary group-containing resin was premixed with the PARAPLEX WP-1. Deionized water was added slowly and carefully with high agitation until the dispersion had thinned sufficiently to add the pigment paste. The remaining water was added relatively quickly with agitation.

The paint prepared as described above had a solids content of about 20 percent, a pH of 6.5 and a conductivity of 1100. Both zinc phosphated and untreated steel panels were electrodeposited with this paint. The coated panels were cured at the various times and temperatures reported in Table III below, scribed and exposed to salt spray as described above in connection with Examples 1 through 7. The results are reported in Table III below as Examples 17-20.

To the paint as described above was added lead lactate so that the paint contained 500 parts per million lead. Both zinc phosphated and untreated steel panels were electrodeposited with this paint. The coated panels were cured at the various times and temperatures reported in Table III below, scribed and exposed to salt spray as discussed above in connection with Examples 1-7. The results are reported in Table III below as Examples 21-24.

A second series of experiments was conducted similar to the first series mentioned immediately above with the exception that the lead silicate and strontium chromate were removed from the paint.

A pigment paste similar to that prepared immediately above but containing no lead silicate nor strontium chromate was prepared from the following charge:

    ______________________________________                                         Ingredient            parts by Weight                                          ______________________________________                                         resinous grinding vehicle.sup.1                                                                      342                                                      deionized water       130                                                      carbon black          29.2                                                     clay                  262.8                                                    dibutyltin oxide      10.2                                                     ______________________________________                                          .sup.1 1600 parts of the resinous grinding vehicle described above thinne      with 1400 parts of deionized water.                                      

The paste was ground in a Jiffy Mill to a Hegman No. 7 grind.

The cationic electrodepositable paints were prepared from the following charge:

    ______________________________________                                         Ingredient              Parts by Weight                                        ______________________________________                                         quaternary ammonium salt group-                                                containing resin        790                                                    PARAPLEX WP-1, plasticizer                                                                             18.0                                                   deionized water         1900                                                   pigment paste with no lead silicate or                                         strontium chromate      316                                                    deionized water         576                                                    ______________________________________                                    

The paint had a solids content of 20 percent, a pH of 6.6 and a conductivity of 1100. Both zinc phosphated and untreated steel panels were electrodeposited with this paint. The coated panels were cured at the various times and temperatures described in Table III below, scribed and exposed to salt spray. The results are reported in Table III below as Examples 25-28.

To the paints as described immediately above was added lead lactate, such that the paint contained 500 parts per million lead. Both zinc phosphated and untreated steel panels were electrodeposited with this paint. The coated panels were cured at the times and temperatures as described in Table III below, scribed and exposed to salt spray. The results are reported in Table III below as Examples 29-32.

                                      Table III                                    __________________________________________________________________________     Effects of Water-Soluble Lead in Cationic Electrodepositable Paints            Example         Bake Schedule                                                                            Film Thickness                                                                         14 Days Salt Spray Exposure,                 No.  Substrate  ° F. (° C.)/minutes                                                        in mils Scribe Creepage                              __________________________________________________________________________     17   zinc phosphated steel                                                                     350° F. (177° C.)/45                                                       0.7     1/32                                         18   untreated steel                                                                           do        0.75     1/8                                         19   zinc phosphated steel                                                                     400° F. (204° C.)/20                                                       0.7     1/32                                         20   untreated steel                                                                           do        0.8      1/8                                         21   zinc phosphated steel                                                                     350° F. (177° C.)/45                                                       0.7     1/32                                         22   untreated steel                                                                           do        0.75    3/64                                         23   zinc phosphated steel                                                                     400° F. (204° C.)/20                                                       0.7     1/32                                         24   untreated steel                                                                           do        0.8     1/16                                         25   zinc phosphated steel                                                                     350° F. (177° C.)/45                                                       0.6     1/32                                         26   untreated steel                                                                           do        1.0      1/8                                         27   zinc phosphated steel                                                                     400° F. (204° C.)/20                                                       0.6     1/32                                         28   untreated steel                                                                           do        1.0     5/32                                         29   zinc phosphated steel                                                                     350° F. (177° C.)/45                                                       0.6     1/32                                         30   untreated steel                                                                           do        0.9     1/32                                         31   zinc phosphated steel                                                                     400° F. (204° C.)/20                                                       0.6     1/32                                         32   untreated steel                                                                           do        0.9     1/32                                         __________________________________________________________________________

EXAMPLES 33-35

A series of experiments were conducted involving the addition of strontium, barium and manganous lactate to aqueous dispersions of cationic electrodepositable resins. The resins were then electrodeposited onto untreated steel panels; the coatings were baked and evaluated for corrosion resistance and appearance.

The cationic electrodepositable resin was an amine salt group-containing resin similar to that of Examples 1-7 prepared from the following charge:

    ______________________________________                                         Ingredient              Parts by Weight                                        ______________________________________                                         EPON 1001               122                                                    normal butyl ketone     44                                                     2-ethylhexyl monourethane of 2,4-                                              toluene diisocyanate    83                                                     dibutyltin dilaurate    0.18                                                   Shell H-1               9.6                                                    diethylamine            11.5                                                   JEFFAMINE D-1000        21.25                                                  hexyl CELLOSOLVE        24.3                                                   deionized water         364                                                    lactic acid (88% in water)                                                                             15.5                                                   ______________________________________                                    

The resin was prepared in the manner generally described above in connection with Examples 1-7.

A pigment grinding vehicle was prepared by blending 321 parts of stearyl glycidyl ether (EPOXIDE 45) and 40 parts of 88 percent aqueous lactic acid and 439 parts of deionized water.

To prepare a pigment paste, 90 parts of this grinding vehicle were blended with 4 parts of SURFYNOL 104-A, 300 parts of deionized water, 198 parts of titanium dioxide and 2 parts of carbon black. The resultant slurry was ground in a Jiffy mill to a Hegman No. 7 grind.

A cationic electrodepositable paint was prepared by mixing in a Cowles mixer the following ingredients:

    ______________________________________                                         Ingredient             Parts by Weight                                         ______________________________________                                         cationic electrodepositable resin                                                                     2896                                                    dibenzyl ether         112                                                     dibutylin dilaurate 11.2                                                       deionized water        2730                                                    pigment paste          795                                                     ______________________________________                                    

Three portions of the cationic electrodepositable paint were diluted with deionized water and combined with strontium, barium and manganous lactate, respectively, to form 12 percent solids electrodeposition baths containing 1000 parts per million strontium, barium and manganese. The pH and conductivities of the baths and appearance of the electrodeposited films on untreated steel panels are reported in Table IV below.

                  Table IV                                                         ______________________________________                                         Electrodeposition Baths Containing Various Lactate Salts                                  Strontium                                                                               Barium    Manganous                                                   Lactate  Lactate   Lactate                                          ______________________________________                                         pH           5.7        5.6       4.7                                          Conductivity 1820       1575      2060                                         Film Apperance                                                                              rough      rough     smooth                                       ______________________________________                                    

The coated panels were subjected to salt spray and were found to be no better in performance than an untreated steel control panel electrocoated with a similar paint but containing no added lactate salt. 

We claim:
 1. An improved method of electrocoating an electrically conductive article serving as a cathode in an electrical circuit comprising an anode, said cathode and an electrodeposition bath comprising an aqueous dispersion of a cationic electrodepositable resin, the improvement comprising the addition to said electrodeposition bath of 50 to 3000 parts per million based on total bath weight of a water-soluble lead compound in an amount sufficient such that it will improve the corrosion resistance of a ferrous metal article which is cathodically electrocoated in said electrodeposition bath, the lead compound being soluble to the extent of at least one percent by weight in water having a pH of
 7. 2. The method of claim 1 in which the water-soluble lead compound is added in an amount sufficient to provide from 100 to 3000 parts per million lead.
 3. The method of claim 1 in which the water-soluble lead compound is the lead salt of an organic acid.
 4. The method of claim 3 in which the water-soluble lead salt is selected from the class consisting of lead acetate and lead lactate.
 5. The method of claim 1 in which the electroconductive article is a ferrous metal article.